Superconductor assembly

ABSTRACT

The invention relates to a superconductor assembly comprising a metallic superconductor and a ceramic superconductor, which are mechanically and electrically interconnected to form a one-piece hybrid superconductor.

[0001] The present invention relates to a superconductor assembly.

[0002] The significance of superconductors continually increases, since conductors capable of carrying high currents even in high magnetic fields are desired in more and more applications. In this case, metallic conductors, such as the superconductor of the type NSTT62000, distributed by Vacuumschmelze, or ceramic superconductors (also called high-temperature superconductors), such as the superconductor of the type Bi-2223HTSL 121-2.3/-AgAgMg, distributed by Vacuumschmelze, are known.

[0003] Due to their low intrinsic specific upper critical magnetic field, the metallic superconductors are not capable of still carrying technically adequate high currents in greater magnetic fields. Due to their upper critical magnetic field, which is much larger than the current permanently accessible magnetic fields, ceramic superconductors have no restriction of this type. The value of the critical current is nearly independent of the external magnetic field above 20 T, for example. However, the ceramic superconductors react more sensitively to mechanical stresses, which are produced in magnets due to the Lorentz force, for example. For these reasons, magnetic systems are frequently segmented into an inner high field segment and an outer segment. In this case, ceramic superconductors are used for the inner high field segment, while metallic superconductors are used for the outer segments. It is problematic in this case to produce a robust, low-loss contact between the individual segments and therefore between metallic superconductors and ceramic superconductors.

[0004] The object of the present invention is therefore to specify a superconductor assembly which does not have these disadvantages.

[0005] This object is achieved by a superconductor assembly according to claim 1. Embodiments and refinements of the idea according to the present invention are the object of the subclaims.

[0006] The advantage of the present invention is that the “monolithic” superconductor assembled from a metallic superconductor and a ceramic superconductor exploits the mechanical properties and the current carrying capacity of the metallic superconductor in the event of low magnetic fields and additionally behaves like a ceramic superconductor in the event of higher magnetic fields.

[0007] This is achieved specifically by a superconductor assembly having a metallic superconductor and a ceramic superconductor, which are mechanically and electrically connected to one another to form a one-piece hybrid superconductor. This means that the two superconductors (particularly composite superconductors) are connected to one another not only at the ends, but are mechanically and electrically connected to one another punctually or continuously over the entire superconductor length.

[0008] In this case, the two superconductors are preferably connected to one another using low-temperature solder. For specific applications, connection using hard solder, conductive plastic (particularly adhesive), or mechanical connection elements (such as clamps, shaped elements, suitable profiles, and special shaping of the superconductors, etc.) is also possible.

[0009] Furthermore, at least one of the two superconductors is preferably provided with a rectangular cross-section and particularly implemented as a strip. Through the rectangular cross-section of the conductors (which is tailored as much as possible), a larger contact surface is provided. This leads to greater mechanical strength of the connection and to a lower electrical resistance.

[0010] For numerous applications of superconductors, they are wound around a core or a carrier, for example. Therefore, the wound superconductors are curved. In a refinement of the present invention, for a curved superconductor assembly according to the present invention, the metallic superconductor has a larger radius of curvature and the ceramic superconductor has a smaller radius of curvature.

[0011] With sufficient mechanical strength of the (soldered) connection, a reversal of the positions of the metallic and the ceramic superconductors is also possible in this case: ceramic superconductor at a larger radius of curvature and metallic superconductor at a smaller radius of curvature. In addition, there is also the possibility of positioning the two superconductors next to one another.

[0012] An A15 compound is provided as the preferred metallic superconductor. A quaternary, externally stabilized NbSn superconductor may be provided as this type of superconductor, which may contain 20%-40% copper (particularly 22%-24% copper). The NbSn superconductor may also be replaced by other metallic high magnetic field conductors, such as NbAl superconductors.

[0013] Preferably, (Bi, Pb)₂Sr₂Ca₂Cu₃O_(x) superconductors are provided as the ceramic superconductor. These superconducting metal oxide compounds have high transition temperatures of at least 77K, because of which these compounds are also referred to as high-temperature superconductor materials and allow cooling by liquid nitrogen. These metal oxide compounds particularly include cuprates based on the bismuth material system Bi—Sr—Ca—Cu—O, individual components of this material system able to be at least partially replaced by others.

[0014] In particular, a corresponding partial substitution of the Bi component by Pb is possible. Within these Bi-containing material systems, at least two superconducting phases arise, which differ in the number of copper-oxygen network planes (layers) within their crystalline unit cells. However, in general, use of all ceramic high-temperature superconductors is conceivable, such as:

[0015] (La, Ba)₂CuO₄;

[0016] (Nd, Ce)₂CuO_(x);

[0017] (Nd, Sr, Ce)₂CuO₄;

[0018] HgBa₂CuO_(x);

[0019] (Pb, Cu) (Eu, Ce)₂(Sr, Eu)₂Cu₂O₉;

[0020] (Eu, Ce)₂(Ba, Eu)₂Cu₃O_(x);

[0021] (Tl, Pb) Sr₄Cu₂CO₃O₇;

[0022] Tl₂Ba₂CuO₆;

[0023] Bi₂Sr₂ (Gd, Ce)₂Cu₂O₁₀;

[0024] Pb₂(Sr, La)₂Cu₂O₆;

[0025] (La, Sr, Ca)₃Cu₂O₆;

[0026] TlBa₂CaCu₂O_(x);

[0027] YBa₂Cu₃O_(x);

[0028] Tl₂Ba₂CaCu₂O₈;

[0029] YBa₂Cu₄O₈;

[0030] Y₂Ba₄Cu₇O₁₅;

[0031] Pb₂Sr₂YCu₃O₈;

[0032] PbBaYSrCu₃O₈;

[0033] TlBa₂Ca₂Cu₃O_(x);

[0034] Tl₂Ba₂Ca₂Cu₃O₁₀;

[0035] (Sr, Ca)₅Cu₅O₁₀;

[0036] TlBa₂Ca₃Cu₄O₁₁;

[0037] Tl₂Ba₂Ca₃Cu₄O₁₂;

[0038] TlBa₂Ca₄Cu₅O₁₃;

[0039] Tl₂Ba₂Ca₄Cu₅O₁₄;

[0040] (Ba, Sr)CuO₂.

[0041] Some elements may also be replaced by other metals (e.g.; Pb) for improved phase formation or the oxygen content may vary.

[0042] If multiple corresponding strip-shaped or wire-shaped high-temperature superconductors or their conductor intermediate products or conductor precursors are bundled in a way known per se, conductors having multiple superconducting conductor cores, multicore or multifilament conductors, may also be obtained. These elements are embedded in a matrix which, in a refinement of the present invention, is preferably made of silver. At the same time, the matrix may be enclosed by a dispersion-hardened silver-magnesium envelope. This envelope provides the multifilament conductor with improvement of its mechanical properties in relation to a pure silver envelope. The characteristic values of tensile stress and extension and radius of curvature for degradation of the critical current are elevated in this case.

[0043] For metallic superconductors, the types NSTxxxxx (xxxxx is the variable filament count between 00001 and 64000, for example), distributed by VAC, may alternatively be used. For the ceramic superconductors, the types having 37, 55, 81, 121, or more filaments, distributed by Vacuumschmelze, may alternatively be used, for example. As a matrix, an Ag alloy may also be used instead of pure silver (e.g.; AgPd_(x) or AgAu_(x)). An AgMn alloy or an AgMgNi alloy may alternatively be used as an envelope, for example.

[0044] The present invention is described in the following in greater detail on the basis of the exemplary embodiments illustrated in the figures of the drawing.

[0045]FIG. 1 shows an exemplary embodiment of a metallic superconductor for use in a superconductor assembly according to the present invention,

[0046]FIG. 2 shows an embodiment of a ceramic superconductor for use in a superconductor assembly according to the present invention,

[0047]FIG. 3 schematically shows the construction of a superconductor assembly according to the present invention in cross-section,

[0048]FIG. 4 shows an exemplary embodiment of a preferred embodiment of a superconductor assembly according to the present invention in a side view, and

[0049]FIG. 5 shows the graph of the current carrying capacity for a single metallic superconductor, a ceramic superconductor, and a superconductor assembly according to the present invention in comparison.

[0050]FIG. 1 shows a cross-section of a conventional, technical, metallic superconductor of the type NSTT62000A23, distributed by Vacuumschmelze. This composite superconductor represents a quaternary, externally stabilized bronze conductor BL having 23% copper, whose construction, together with the heat treatment used during manufacture, is optimized for high field usage.

[0051]FIG. 2 shows a cross-section of a ceramic superconductor (high-temperature superconductor) of the type Bi-2223 HTSL 121-2.3/-AgAgMg, distributed by Vacuumschmelze. This superconductor contains a reacted high-temperature superconductor cuprate of the type Bi-2223 in 121 filaments FL. Specifically, Bi₂Sr₂Ca₂Cu₃O_(x) is used as the cuprate, bismuth able to be partially replaced by lead. These filaments FL are embedded in a matrix AG made of silver, which is in turn enclosed by a dispersion-hardened silver-magnesium envelope HL. Such a ceramic composite superconductor has, for example, a critical current Ic=55-80 A at a temperature of T=77K, and an electrical field Ec=1 μV/cm in the intrinsic magnetic field.

[0052] As shown in FIG. 3, according to the present invention, a metallic superconductor MSL, such as that shown in FIG. 1, and a ceramic superconductor HTS, such as that shown in FIG. 2, are mechanically and electrically connected to one another via a solder connection LV. For example, low melting point, commercially obtainable solder of the type ELSOLD soft solder S—Bi50, Pb25Sn12, 5Cd12.5, or α-Grillo solder tin Ni49In21Pb18Sn12, or Fusion Solder Paste SSX-430-830, among others, may be used as the solder.

[0053] To solder the two superconductors MSL and HTS, the solder LV is applied as a paste between the two layers, for example, and the entire assembly is subsequently appropriately heated. Another possibility is to pour a liquid solder LV between the heated superconductors MSL and HTSL. Hard soldering using a NiCoSn film is also possible.

[0054] A winding produced using a superconductor assembly according to the present invention is shown in a side view in FIG. 4. The winding is applied to a winding carrier WT in this case. Winding carrier WT and the superconductor arrangement are essentially round, so that the superconductor arrangement has a corresponding curvature. In this case, the ceramic superconductor HTS is positioned closer to the carrier WT than the metallic superconductor MSL, for example.

[0055] In FIG. 5, the current carrying capacity of a single metallic superconductor MSL, a ceramic superconductor HTSL, and a hybrid composite superconductor according to the present invention are shown in comparison. The graph of the ceramic superconductor HTS starts out falling steeply from high current densities I_(c) (in A) and small magnetic fluxes B (in T) in this case and then passes in a flatter curve to smaller current densities. In contrast, the graph of the metallic superconductor MSL begins at moderate magnetic fluxes B and high current densities and practically approaches zero at high magnetic fluxes B, the curve being essentially steep.

[0056] It may be seen from this that the metallic superconductors MSL are not still capable of carrying technically adequate high currents in larger magnetic field. The ceramic superconductors HTS, in contrast, have no restriction of this type. The value of the critical current for ceramic superconductors is nearly independent of the external magnetic field above 20 T, for example. However, the ceramic superconductors react more sensitively to mechanical strains, which may be produced in magnet end axes and through the Lorentz force, for example.

[0057] The present invention reduces these problems significantly, in that it connects metallic superconductors MSL and ceramic superconductors HTS into a monolithic conductor in such a way that the current carrying capacity of the metallic superconductor MSL is exploited in low magnetic fields and the current carrying capacity of the ceramic superconductor HTS is then used in higher magnetic fields.

[0058] A further advantage in this case is that the maximum of the force strain (Lorentz force) now no longer arises in the highest fields (>20 T), but rather at approximately 15 T. As may be seen from FIG. 5, the Ic(B) curve for the hybrid composite superconductor is shaped in such a way that it does not approach zero in stronger magnetic fields, but rather turns into the curve of the ceramic superconductors HTS at larger currents. 

1. A superconductor assembly having a metallic superconductor (MSL) and a ceramic superconductor (HTS), which are mechanically and electrically connected to one another to produce a one-piece hybrid superconductor.
 2. The superconductor assembly according to claim 1, wherein the two superconductors (MSL, HTS) are connected to one another using low-temperature solder (LV).
 3. The superconductor assembly according to one of the preceding claims, wherein at least one of the two superconductors (MSL, HTS) has a rectangular cross-section.
 4. The superconductor assembly according to one of the preceding claims, wherein the two superconductors (MSL, HTS) connected to one another are curved, the metallic superconductor (MSL) having a greater radius of curvature than the ceramic superconductor (HTS) or vice versa.
 5. The superconductor assembly according to one of the preceding claims, wherein an A15 compound is provided as the metallic superconductor (MSL).
 6. The superconductor assembly according to claim 7, wherein a quaternary, externally stabilized bronze conductor is provided as the NbSn superconductor.
 7. The superconductor assembly according to claim 8, wherein the bronze conductor contains 20 to 40 percent copper.
 8. The superconductor assembly according to one of the preceding claims, wherein a (Bi, Pb)₂Sr₂Ca₂Cu₃O_(x) superconductor is provided as the ceramic superconductor (HTS).
 9. The superconductor assembly according to claim 8, wherein the superconductor (HTS) has multiple filaments (FL) which are embedded in a matrix (AG) made of silver.
 10. The superconductor assembly according to claim 9, wherein the matrix (AG) is enclosed by a dispersion-hardened silver-magnesium envelope (HL). 